PARSICAST 50Al

Description: Hydraulic bond high alumina castable


:Chemical analysis
%Al2O3..............................................................................................    50    
%SiO2 ................................................................................................    30    
%TiO2 ................................................................................................    2.5    
%Fe2O3.............................................................................................    5.5    
%CaO ................................................................................................    10    
%Alkalies (Na2O+K2O) ...................................................................    1    

   
:Physical data
Maximum service temperature, (oC).............................................    1420
(Grain size(mm).................................................................................    (0-5)&(0-6.3
Dry castable required (ton/m3).......................................................    2.1
Water required, (%)............................................................................    12
Bulk density, (g/cm3) After drying at 110 oC..................................    2.35
(Modulus of rupture (Kgf/cm2
After drying at 110 oC..........................................    40                               
After heating at 900 oC.......................................    35                              
After firing at 1350 oC........................................    55                               
(Cold crushing strength (Kgf/cm2
After drying at 110 oC............................................   500                             
After heating at 900 oC........................................    400                             
After firing at 1350 oC..........................................    450                             
(%)Linear change
After drying at 110 oC..........................................    Negligible                             
After heating at 900 oC.......................................    +0.05                             
After firing at 1350 oC........................................    +0.15                             
The above mentioned data represent typical values obtained from current production, according to JIS test method
All data are subjected to reasonable variations, and therefore, should not be used for specification purposes, guarantees in respect of these data are only valid if agreed upon in writing

:Storage & Stacking limit
Dry stored approx. 8 months
To avoid the compaction of mixes do not store more than 3 pallets above each other


:Packing
In multi – wall, moisture proof sacks of 40 kg, net weight. on wooden pallet, fastened by 4 vertical belts, 180 micron shrink film on it

 