PARSITAL 98SD

Classification: Direct bond Magnesia brick

:Chemical analysis
%MgO ....................................................................................     96    
%Al2O3 ..................................................................................    0.5    
%Fe2O3 .................................................................................    0.5    
%CaO ....................................................................................     1.5    
%SiO2   .................................................................................      1    

:Physical data

Bulk density (g/cm3) ................................................................    2.85
Apparent porosity (%) ...............................................................    19
Cold crushing strength (Kgf/cm2) .........................................    650
Hot modulus of rupture (Kgf/cm2 at 1000 oC) .....................    100
Thermal conductivity (W/mok at 350 oC) ............................    3.5
at 1000 oC) ...........................................    2.9)                                      
Lin. thermal expansion (% at 1000 oC) ...................................    1.33
Refractoriness under load (T2 , oC) .......................................    1650
The above mentioned data represent typical values obtained from current production, according to JIS test method
All data are subjected to reasonable variations, and therefor, should not be used for specification purposes, guarantees in respect of these data are only valid if agreed upon in writing

:Application
Hot metal mixer, EAF, LD Converter, Lime furnace, regenerators of glass furnace

:Packing
Bricks on wooden pallet, each pallet app . 1.2 – 1.4 MT. Fastened by 4 vertical belts, 180 micron shrink film on it