PARSIMIX K
Description: Universal mix manufactured from dead burned magnesia, Chemical bond
:Chemical analysis
%MgO................................92
Al2O3..............................1%
Fe2O3..............................1%
CaO..................................4%
SiO2..................................4
:Physical data
Maximum service temperature, ( oC)....................1750
Maximum grain size, ( mm )...................................2
Consumption, (Tons/m3, Typical ),........................2.5
Cold crushing strength (Kgf/cm2),
after drying at 110 oC...........................................400
after firing at 1300 oC..........................................150
The above mentioned data represent typical values obtained from current production, according to JIS test method
All data are subjected to reasonable variations, and therefore, should not be used for specification purposes, guarantees in respect of these data are only valid if agreed upon in writing
:Preparation
Addition of water, approx. 20% by weight. Parsimix always to be stirred into the water, avoid lump formation. Mortar stirring devices facilitate homogenization.The mix is ready for use after 12 minutes and remains in workable condition for several hours
:Storage limit
Dry stored, approx. 6 months
:Packing
In multi – wall, moisture proof sacks of 40Kg, net weight or 1 MT. Big bags on wooden pallet, fastened by 4 vertical belts, 180 micron shrink film on it